A2 Stainless Steel SEMS Screws with Captive Conical Spring Washers combine the dimensional form of DIN 6900-5 Z9 and DIN 6908 with the material properties of grade ISO 3506 group A2 (304 / 1.4301), commonly supplied A2-70: good general corrosion resistance, largely non-magnetic, service range approx. -200 °C to +400 °C, subject to the property class and the joint. This page summarizes the grade data, its corrosion behavior in service, the comparable grades, and the sizes supplied.
Why Choose A2 Stainless Steel for SEMS Screws with Captive Conical Spring Washers
The most common stainless group for indoor and general outdoor fasteners. For sems screws with captive conical spring washers, this matters when good general corrosion resistance is the primary requirement.
Mechanical & Physical Properties
| Grade designation | ISO 3506 group A2 (304 / 1.4301), commonly supplied A2-70 |
|---|---|
| Magnetic response | Largely non-magnetic |
| Service temperature | approx. -200 °C to +400 °C, subject to the property class and the joint |
| Corrosion characteristic | Good general corrosion resistance |
Galvanic & Galling Considerations
Two important notes for stainless sems screws with captive conical spring washers: (1) stainless can gall on stainless threads under load — use a thread lubricant or anti-galling compound, especially for M6 and below; (2) when joined to aluminum or galvanized steel, stainless can drive galvanic corrosion of the less-noble metal in wet service — isolate with a coating or sleeve where appropriate.
Comparable Grades
For SEMS Screws with Captive Conical Spring Washers, the alternative stainless grade is A4 (316). A2 (304) suits general indoor and outdoor service; A4 (316) adds molybdenum for marine and chloride environments. Where higher strength matters more than corrosion, switch to plated alloy-steel class 8.8 or 10.9.
Using Stainless Fasteners in Aluminum
Stainless steel is more noble than aluminum, so in the presence of an electrolyte — rain, condensation, salt spray — the aluminum becomes the anode and corrodes at the joint. The effect is driven by the area ratio: a small stainless fastener in a large aluminum section is normally acceptable, while a large stainless fastener in thin aluminum is not. Where the joint is wet, isolate the two metals with a coated or nylon washer and a sealant, or specify an aluminum or coated fastener instead.
Sizes of SEMS Screws with Captive Conical Spring Washers Available in A2 Stainless Steel
| Thread size | Pitch (mm) | Washer inside diameter (mm) | Washer outside diameter (mm) | Washer thickness (mm) | Material options | Reference standard |
|---|---|---|---|---|---|---|
| M2.5 | 0.45 | 2.25~2.35 | 5.7~6.0 | 0.5 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M3 | 0.5 | 2.75~2.85 | 6.64~7.0 | 0.6 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M4 | 0.7 | 3.6~3.72 | 8.64~9.0 | 1.0 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M5 | 0.8 | 4.55~4.67 | 10.57~11.0 | 1.2 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M6 | 1.0 | 5.5~5.62 | 13.57~14.0 | 1.5 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M8 | 1.25 | 7.4~7.55 | 17.57~18.0 | 2.0 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M10 | 1.5 | 9.3~9.45 | 22.48~23.0 | 2.5 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |
| M12 | 1.75 | 11.0~11.18 | 28.48~29.0 | 3.0 | steel or A2 stainless | DIN 6900-5 Z9 and DIN 6908 |